  • Title: Biodegradable recombinant human erythropoietin loaded microspheres prepared from linear and star-branched block copolymers: influence of encapsulation technique and polymer composition on particle characteristics.
    Author: Pistel KF, Bittner B, Koll H, Winter G, Kissel T.
    Journal: J Control Release; 1999 Jun 02; 59(3):309-25. PubMed ID: 10332063.
    Abstract:
    Recombinant human erythropoietin (EPO) and fluorescein isothiocyanate labeled dextran (FITC-dextran) loaded microspheres were prepared by a modified W/O/W double-emulsion technique. Biodegradable linear ABA block copolymers consisting of poly(L-lactide-co-glycolide) A blocks attached to central poly(ethyleneoxide) (PEO) B blocks and star-branched AB block copolymers containing A blocks of poly(L-lactide) or poly(L-lactide-co-glycolide) and star-branched poly(ethyleneoxide) B blocks were investigated for their potential as sustained release drug delivery systems. Microsphere characteristics were strongly influenced by the polymer composition. In the case of the linear block copolymers, a reduced lactic acid content in a linear block copolymer yielded smaller particles, a lower encapsulation efficiency, and a higher initial drug release both in the case of EPO and FITC-dextran. The investigation of the effects of several manufacturing parameters on microsphere formation showed that the process temperature plays an important role. Microsphere formation in a +1 degrees C environment resulted in higher drug loadings without increasing the amount of residual dichloromethane inside the particles. Other parameters such as the homogenization of the primary W/O emulsion and of the W/O/W double-emulsion have less impact on microsphere characteristics. Branched block copolymers containing star-shaped PEO also showed potential for the preparation of drug loaded microspheres. A certain amount of glycolic acid in the copolymer was necessary for the successful preparation of non-aggregating microspheres at room temperature. Again, the processing temperature strongly affected particle characteristics. Microsphere preparation at +1 degrees C allows the formation of microspheres from a polymer not containing glycolic acid, a result which could not be achieved at room temperature. Moreover, compared to microsphere formation at room temperature, the effective FITC-dextran loading was increased. Concerning the EPO loaded microspheres, the amount of EPO aggregated was comparable to that using the linear ABA polymers. A continuous release of the protein from these star-shaped polymers could not be achieved. In conclusion, apart from microsphere preparation in a +1 degrees C environment the choice of the polymer represents the main factor for a successful entrapment of proteins into biodegradable microspheres.
    [Abstract] [Full Text] [Related] [New Search]