These tools will no longer be maintained as of December 31, 2024. Archived website can be found here. PubMed4Hh GitHub repository can be found here. Contact NLM Customer Service if you have questions.


Pubmed for Handhelds

PUBMED FOR HANDHELDS

Search MEDLINE/PubMed

  • Title: The use of an injectable, biodegradable calcium phosphate bone substitute for the prophylactic augmentation of osteoporotic vertebrae and the management of vertebral compression fractures.
    Author: Bai B, Jazrawi LM, Kummer FJ, Spivak JM.
    Journal: Spine (Phila Pa 1976); 1999 Aug 01; 24(15):1521-6. PubMed ID: 10457570.
    Abstract:
    STUDY DESIGN: A biomechanical study comparing two materials for augmentation of osteoporotic vertebral bodies and vertebral bodies after compression fracture. OBJECTIVES: To compare an injected, biodegradable calcium phosphate bone substitute with injected polymethylmethacrylate bone cement for strengthening osteoporotic vertebral bodies and improving the integrity of vertebral compression fractures. SUMMARY OF BACKGROUND DATA: Injection of polymethylmethacrylate bone cement into fractured vertebral bodies has been used clinically. However, there is concern about thermal damage to the neural elements during polymerization of the polymethylmethacrylate bone cement as well as its negative effects on bone remodeling. Biodegradable calcium phosphate bone substitutes have been studied for enhancement of fixation in fractured vertebrae. METHODS: Forty fresh osteoporotic thoracolumbar vertebrae were used for two separate parts of this study: 1) injection into osteoporotic vertebrae: intact control (n = 8), calcium phosphate (n = 8), and polymethylmethacrylate bone cement (n = 8) groups. Each specimen then was loaded in anterior compression until failure; 2) injection into postfractured vertebrae: calcium phosphate (n = 8) and polymethylmethacrylate bone cement (n = 8) groups. Before and after injection, the specimens were radiographed in the lateral projection to determine changes in vertebral body height and then loaded to failure in anterior bending. RESULTS: For intact osteoporotic vertebrae, the average fracture strength was 527 +/- 43 N (stiffness, 84 +/- 11 N/mm), 1063 +/- 127 N (stiffness, 157 +/- 21 N/mm) for the group injected with calcium phosphate, and 1036 +/- 100 N (stiffness, 156 +/- 8 N/mm) for the group injected with polymethylmethacrylate bone cement. The fracture strength and stiffness in the calcium phosphate bone substitute group and those in the polymethylmethacrylate bone cement group were similar and significantly stronger than those in intact control group (P < 0.05). For the compression fracture study, anterior vertebral height was increased 58.5 +/- 4.6% in the group injected with calcium phosphate and 58.0 +/- 6.5% in the group injected with polymethylmethacrylate bone cement as compared with preinjection fracture heights. No significant difference between the two groups was found in anterior vertebral height, fracture strength, or stiffness. CONCLUSION: This study demonstrated that the injection of a biodegradable calcium phosphate bone substitute to strengthen osteoporotic vertebral bodies or improve vertebral compression fractures might provide an alternative to the use of polymethylmethacrylate bone cement.
    [Abstract] [Full Text] [Related] [New Search]