  • Title: A 6-year clinical evaluation of Class I poly-acid modified resin composite/resin composite laminate restorations cured with a two-step curing technique.
    Author: van Dijken JW.
    Journal: Dent Mater; 2003 Jul; 19(5):423-8. PubMed ID: 12742438.
    Abstract:
    OBJECTIVE: Polymerization shrinkage is still one of the main disadvantages of resin composite restorations (RC). Especially in cavities with a high C-factor, debonding can occur. A laminate restoration including a base with a more elastic behavior might result in a better adaptation. The purpose of this study was to evaluate the durability of a combination of two techniques suggested to counter the stress formation in direct RC restorations in cavities with the highest C-factor. METHODS: Each of the 29 patients received one or two pair(s) of Class I restorations. The first restoration was a poly-acid modified resin composite/resin composite (PMRC/RC) sandwich restoration and the second a direct RC restoration. Both restorations, except for the PMRC layer, were placed with oblique layering and two-step curing technique. Ninety restorations, 23 premolar and 67 molars, were evaluated annually with slightly modified USPHS criteria during 6 years. RESULTS: At 6 years, 41 pairs were evaluated. A cumulative failure rate of 2.4% was observed for both the RC and the laminate restorations. One laminate restoration showed non-acceptable color match, but was not replaced and one RC restoration showed non-acceptable marginal adaptation. Two cases of slight postoperative sensitivity were observed in one patient. Three restorations were partially replaced due to primary proximal caries. SIGNIFICANCE: A high durability for and no differences, were observed between both restorative techniques in Class I cavities.
    [Abstract] [Full Text] [Related] [New Search]