  • Title: Low-temperature destruction of carbon tetrachloride over lanthanide oxide-based catalysts: from destructive adsorption to a catalytic reaction cycle.
    Author: Van der Avert P, Podkolzin SG, Manoilova O, de Winne H, Weckhuysen BM.
    Journal: Chemistry; 2004 Apr 02; 10(7):1637-46. PubMed ID: 15054750.
    Abstract:
    The catalytic destruction of carbon tetrachloride in the presence of steam, CCl(4) + 2 H(2)O-->4 HCl + CO(2), was investigated at 200-350 degrees C over a series of lanthanide (La, Ce, Pr and Nd) and alkaline-earth metal (Mg, Ca, Sr and Ba) oxide-based catalysts with kinetic experiments, Raman spectroscopy, X-ray photoelectron spectroscopy, IR spectroscopy, X-ray diffraction, and DFT calculations. This new catalytic reaction was achieved by combining destructive adsorption of CCl(4) on a basic oxide surface and concurrent dechlorination of the resulting partially chlorinated solid by steam. The combination of the two noncatalytic reactions into a catalytic cycle provided a rare opportunity in heterogeneous catalysis for studying the nature and extent of surface participation in the overall reaction chemistry. The reaction is proposed to proceed over a terminal lattice oxygen site with stepwise donation of chlorine atoms from the hydrocarbon to the surface and formation of the gas-phase intermediate COCl(2), which is readily readsorbed at the catalyst surface to form CO(2). In a second step, the active catalyst surface is regenerated by steam with formation of gas-phase HCl. Depending on the reaction conditions, the catalytic material was found to transform dynamically from the metal oxide state to the metal oxide chloride or metal chloride state due to the bulk diffusion of oxygen and chlorine atoms. A catalyst obtained from a 10 wt % La(2)O(3)/Al(2)O(3) precursor exhibited the highest destruction rate: 0.289 g CCl(4) h(-1) g(-1) catalyst at 350 degrees C, which is higher than that of any other reported catalyst system.
    [Abstract] [Full Text] [Related] [New Search]