  • Title: Preparation of magnesium-substituted hydroxyapatite powders by the mechanochemical-hydrothermal method.
    Author: Suchanek WL, Byrappa K, Shuk P, Riman RE, Janas VF, TenHuisen KS.
    Journal: Biomaterials; 2004 Aug; 25(19):4647-57. PubMed ID: 15120511.
    Abstract:
    Magnesium-substituted hydroxyapatite (Mg-HAp) powders with different crystallinity levels were prepared at room temperature via a heterogeneous reaction between Mg(OH)(2)/Ca(OH)(2) powders and an (NH(4))(2)HPO(4) solution using the mechanochemical-hydrothermal route. The as-prepared products contained unreacted Mg(OH)(2) and therefore had to undergo purification in ammonium citrate aqueous solutions at room temperature. X-ray diffraction, infrared spectroscopy, thermogravimetric and chemical analyses were performed and it was determined that the purified powders were phase-pure Mg-HAp containing 0.24-28.4 wt% of Mg. The concentration of Mg was slightly lower near the surface than in the bulk of the HAp crystals as indicated by X-ray photoelectron spectroscopy. Dynamic light scattering revealed that the median particle size of the room temperature Mg-HAp powders was in the range of 102 nm-1.2 microm with a specific surface area between 91 and 269 m(2)/g. Scanning electron microscopy confirmed that the Mg-HAp powders consisted of submicron agglomerates of nanosized crystals, less than approximately 20 nm.
    [Abstract] [Full Text] [Related] [New Search]