  • Title: Solution-processed silicon films and transistors.
    Author: Shimoda T, Matsuki Y, Furusawa M, Aoki T, Yudasaka I, Tanaka H, Iwasawa H, Wang D, Miyasaka M, Takeuchi Y.
    Journal: Nature; 2006 Apr 06; 440(7085):783-6. PubMed ID: 16598254.
    Abstract:
    The use of solution processes-as opposed to conventional vacuum processes and vapour-phase deposition-for the fabrication of electronic devices has received considerable attention for a wide range of applications, with a view to reducing processing costs. In particular, the ability to print semiconductor devices using liquid-phase materials could prove essential for some envisaged applications, such as large-area flexible displays. Recent research in this area has largely been focused on organic semiconductors, some of which have mobilities comparable to that of amorphous silicon (a-Si); but issues of reliability remain. Solution processing of metal chalcogenide semiconductors to fabricate stable and high-performance transistors has also been reported. This class of materials is being explored as a possible substitute for silicon, given the complex and expensive manufacturing processes required to fabricate devices from the latter. However, if high-quality silicon films could be prepared by a solution process, this situation might change drastically. Here we demonstrate the solution processing of silicon thin-film transistors (TFTs) using a silane-based liquid precursor. Using this precursor, we have prepared polycrystalline silicon (poly-Si) films by both spin-coating and ink-jet printing, from which we fabricate TFTs with mobilities of 108 cm2 V(-1) s(-1) and 6.5 cm2 V(-1) s(-1), respectively. Although the processing conditions have yet to be optimized, these mobilities are already greater than those that have been achieved in solution-processed organic TFTs, and they exceed those of a-Si TFTs (< or = 1 cm2 V(-1) s(-1)).
    [Abstract] [Full Text] [Related] [New Search]