  • Title: The influence of the crystallinity of electrostatic spray deposition-derived coatings on osteoblast-like cell behavior, in vitro.
    Author: Siebers MC, Walboomers XF, Leeuwenburgh SC, Wolke JG, Jansen JA.
    Journal: J Biomed Mater Res A; 2006 Aug; 78(2):258-67. PubMed ID: 16628711.
    Abstract:
    This article describes the influence of the crystallinity of carbonate apatite (CA) coatings on osteoblast-like cell behavior. Porous CA coatings were produced with electrostatic spray deposition (ESD), and subsequently, received heat treatments of 400, 500, or 700 degrees C to induce various coating crystallinities. As a result, an amorphous calcium phosphate (ACP), a crystalline CA (CCA), and a crystalline carbonated hydroxyapatite (CHA) structure were formed, respectively. Uncoated titanium substrates served as the control group. After seeding rat osteoblast-like cells, the initial cell attachment was similar between the groups, and approached 100% after 6 h. Between the various coatings, no differences were observed for proliferation, differentiation, or mineralization. However, proliferation of the osteoblast-like cells was lower on all coated substrates after longer culture periods, compared to the uncoated substrates, while at the same time differentiation was stimulated. Furthermore, after 8 and 16 days of incubation, scanning electron microscopy showed more signs of mineralization on coated substrates, compared to the uncoated substrates. In conclusion, porous ESD-derived CA coatings have a positive effect on the in vitro differentiation of osteoblast-like cells, compared to uncoated, as-machined titanium. However, this effect is not further enhanced by the degree of crystallinity of the ESD-derived CA coatings.
    [Abstract] [Full Text] [Related] [New Search]