  • Title: Sol-gel fabrication and photoluminescence properties of SiO2 @ Gd2O3:Eu3+ core-shell particles.
    Author: Li GZ, Yu M, Wang ZL, Lin J, Wang RS, Fang J.
    Journal: J Nanosci Nanotechnol; 2006 May; 6(5):1416-22. PubMed ID: 16792374.
    Abstract:
    A uniform nanolayer of europium-doped Gd2O3 was coated on the surface of preformed submicron silica spheres by a Pechini sol-gel process. The resulted SiO2 @ Gd2O3:Eu3+ core-shell structured phosphors were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), photoluminescence (PL) spectra as well as kinetic decays. The XRD results show that the Gd2O3:Eu3+ layers start to crystallize on the SiO2 spheres after annealing at 400 degrees C and the crystallinity increases with raising the annealing temperature. The core-shell phosphors possess perfect spherical shape with narrow size distribution (average size: 640 nm) and non-agglomeration. The thickness of the Gd2O3:Eu3+ shells on the SiO2 cores can be adjusted by changing the deposition cycles (70 nm for three deposition cycles). Under short UV excitation, the obtained SiO2@Gd2O3:Eu3+ particles show a strong red emission with 5D0-7F2 (610 nm) of Eu3+ as the most prominent group. The PL intensity of Eu3+ increases with increasing the annealing temperature and the number of coating cycles.
    [Abstract] [Full Text] [Related] [New Search]