  • Title: Comparison of the retentive characteristics of cobalt-chromium and commercially pure titanium clasps using a novel method.
    Author: Tse ET, Cheng LY, Luk HW, Chu FC, Chai J, Chow TW.
    Journal: Int J Prosthodont; 2006; 19(4):371-2. PubMed ID: 16900820.
    Abstract:
    This study aimed to compare the retentive forces of cast cobalt-chromium (Co-Cr) and commercially pure titanium (cpTi) clasps. A clasp assembly comprising a pair of symmetrical clasps was made to fit the opposite halves of a hardened stainless-steel sphere. This twin clasp was designed to counterbalance the tipping forces when the clasp assembly was drawn from the sphere. A total of 120 clasp assemblies were fabricated in cast Co-Cr and cpTi and placed at undercut depths of 0.25 mm, 0.50 mm, and 0.75 mm (n = 20 for each). For Co-Cr clasps, the retentive forces at these undercuts depths were 2.34 +/- 0.23 N, 4.65 +/- 0.35 N, and 7.56 +/- 0.50 N, respectively. The corresponding retentive forces for cpTi clasps were 1.24 +/- 0.13 N, 2.34 +/- 0.23 N, and 3.70 +/- 0.27 N. The retentive force of cpTi clasps was approximately half that of Co-Cr clasps for the same undercut depth.
    [Abstract] [Full Text] [Related] [New Search]