  • Title: The effectiveness of different polymerization protocols for class II composite resin restorations.
    Author: de Jong LC, Opdam NJ, Bronkhorst EM, Roeters JJ, Wolke JG, Geitenbeek B.
    Journal: J Dent; 2007 Jun; 35(6):513-20. PubMed ID: 17383067.
    Abstract:
    OBJECTIVES: To investigate the effect of reduced light exposure times on Vickers hardness (VH) of class II composite resin restorations. METHODS: Class II restorations were made in vitro in three 2mm thick increments in a human molar. Two composite resins (Clearfil AP-X; Esthet-X) were polymerized with four light-curing units (Halogen; Astralis 10, LED; The Cure, L.E. Demetron I, Smartlite) following four curing protocols. Three protocols with exposure times of 10s, 20s or 40s (control) per layer. In the fourth protocol, 10s irradiation per layer was combined with additional lateral curing for 10s from buccal and palatal after removal of the metal matrix. VH of the axial surface was determined at top and bottom layers directly after light-curing and after 7 days storage. Linear regression analysis was performed to analyze the effect of protocol variables. RESULTS: Directly after light-curing VH of both composite resins was significantly influenced by curing protocols. After 7 days, curing protocols had no significant effect on VH of Clearfil AP-X, except for the Smartlite. VH of Esthet-X was still influenced by curing protocol, but differences were smaller than directly after light-curing. CONCLUSIONS: With high intensity light-curing units, exposure times of 10s/2mm increment can be sufficient to obtain under in vitro conditions a high degree of conversion, depending on materials and curing protocols. With additional lateral curing of a class II composite resin restoration a higher degree of cure can be obtained in less time.
    [Abstract] [Full Text] [Related] [New Search]