  • Title: Short glass fiber-reinforced composite with a semi-interpenetrating polymer network matrix for temporary crowns and bridges.
    Author: Garoushi SK, Vallittu PK, Lassila LV.
    Journal: J Contemp Dent Pract; 2008 Jan 01; 9(1):14-21. PubMed ID: 18176644.
    Abstract:
    AIMS: The purpose of this study was to investigate the reinforcement effect of short E-glass fiber fillers on some mechanical properties of temporary crown and bridge (TCB) composite resin with a semi-interpenetrating polymer network (semi-IPN). METHODS AND MATERIALS: Experimental temporary fiber reinforced (TFC) composite resin was prepared by mixing 15 wt% of short E-glass fibers (3 mm in length) with a 35 wt% of semi-IPN-resin (dual or chemical cure) with 50 wt% of silane treated particulate silica fillers using a high speed mixing device. Temporary crowns (n=6) and test specimens (2 x 2 x 25 mm3) (n=6) were made from the experimental TFC and conventional TCB composite (control, Protemp Garant, 3M-ESPE, St. Paul, MN, USA). A three-point bending test was done according to ISO standard 10477, and a compression loading test was carried out using a steel ball (Ø 3.0 mm) with a speed of 1.0 mm/min until fracture occurred. The degree of monomer conversion (DC%) of both composites was determined by Fourier transfer infrared (FTIR) spectrometry. RESULTS: The analysis of variance (ANOVA) revealed both dual and chemical cure experimental TFC composite resins had statistically significant (p<0.05) higher flexural strengths (117 and 99 MPa, respectively) and compressive load-bearing capacity (730 and 623 N, respectively) compared to the control TCB composite resin (72 MPa, 549 N). CONCLUSION: The use of short fiber fillers with semi-IPN polymer matrix yielded an improved mechanical performance compared to a conventional TCB composite resin.
    [Abstract] [Full Text] [Related] [New Search]