  • Title: Skeletal Ru/Cu catalysts prepared from crystalline and quasicrystalline ternary alloy precursors: characterization by X-ray absorption spectroscopy and CO oxidation.
    Author: Highfield J, Liu T, Loo YS, Grushko B, Borgna A.
    Journal: Phys Chem Chem Phys; 2009 Feb 28; 11(8):1196-208. PubMed ID: 19209363.
    Abstract:
    The Ru/Cu system is of historical significance in catalysis. The early development and application of X-ray absorption spectroscopy (XAS) led to the original 'bimetallic cluster" concept for highly-immiscible systems. This work explores alkali leaching of Al-based ternary crystalline and quasicrystalline precursors as a potential route to bulk Ru/Cu alloys. Single-phase ternary alloys at 3 trial compositions; Al(71)Ru(22)Cu(7), Al(70.5)Ru(17)Cu(12.5), and Al(70)Ru(10)Cu(20), were prepared by arc melting of the pure metal components. After leaching, the bimetallic residues were characterized principally by transmission XAS, "as-leached" and after annealing in H(2) (and passivation) in a thermobalance. XRD and BET revealed a nanocrystalline product with a native structure of hexagonal Ru. XPS surface analysis of Ru(22)Cu(7) and Ru(17)Cu(12.5) found only slight enrichment by Cu in the as-leached forms, with little change upon annealing. Ru(10)Cu(20) was highly segregated as-leached. XANES data showed preferential oxidation of Cu in Ru(22)Cu(7), implying that it exists as an encapsulating layer. TG data supports this view since it does not show the distinct two-stage O(2) uptake characteristic of skeletal Ru. Cu K-edge EXAFS data for Ru(22)Cu(7) were unique in showing a high proportion of Ru neighbours. The spacing, d(CuRu) = 2.65 A, was that expected from a hypothetical (ideal) solid solution at this composition, but this is unlikely in such a bulk-immiscible system and Ru K-edge EXAFS failed to confirm bulk alloying. Furthermore its invariance under annealing was more indicative of an interfacial bond between bulk components, although partial alloying with retention of local order cannot entirely be ruled out. The XAS and XPS data were reconciled in a model involving surface and bulk segregation, Cu being present at both the grain exterior and in ultra-fine internal pores. This structure can be considered as the 3-dimensional analogue of the classical type. Preliminary studies in CO and H(2) oxidation were made in a DRIFTS flow reactor with on-line MS, and their activities and selectivities were compared against skeletal Ru and Cu controls, Ru/Al(2)O(3), and Au/Fe(2)O(3). All samples were active in CO oxidation above approximately 50 degrees C, showing light-off temperatures in the range 60-70 degrees C. Ru(22)Cu(7) and Ru(17)Cu(12.5) also showed good selectivities (vs. H(2) oxidation), attributed tentatively to Ru-modified Cu surfaces of varying thickness. These compositions are promising candidates to test in a (PROX) fuel processor to supply purified (CO-free) H(2) to a PEM fuel cell.
    [Abstract] [Full Text] [Related] [New Search]