  • Title: Biocompatibility of corrosion-resistant zeolite coatings for titanium alloy biomedical implants.
    Author: Bedi RS, Beving DE, Zanello LP, Yan Y.
    Journal: Acta Biomater; 2009 Oct; 5(8):3265-71. PubMed ID: 19433139.
    Abstract:
    Titanium alloy, Ti6Al4V, is widely used in dental and orthopedic implants. Despite its excellent biocompatibility, Ti6Al4V releases toxic Al and V ions into the surrounding tissue after implantation. In addition, the elastic modulus of Ti6Al4V ( approximately 110GPa) is significantly higher than that of bone (10-40GPa), leading to a modulus mismatch and consequently implant loosening and deosteointegration. Zeolite coatings are proposed to prevent the release of the toxic ions into human tissue and enhance osteointegration by matching the mechanical properties of bone. Zeolite MFI coatings are successfully synthesized on commercially pure titanium and Ti6Al4V for the first time. The coating shows excellent adhesion by incorporating titanium from the substrate within the zeolite framework. Higher corrosion resistance than the bare titanium alloy is observed in 0.856M NaCl solution at pHs of 7.0 and 1.0. Zeolite coatings eliminate the release of cytotoxic Al and V ions over a 7 day period. Pluripotent mouse embryonic stem cells show higher adhesion and cell proliferation on the three-dimensional zeolite microstructure surface compared with a two-dimensional glass surface, indicating that the zeolite coatings are highly biocompatible.
    [Abstract] [Full Text] [Related] [New Search]