  • Title: A suitable base material for composite resin restorations: zinc oxide eugenol.
    Author: He LH, Purton DG, Swain MV.
    Journal: J Dent; 2010 Apr; 38(4):290-5. PubMed ID: 19961894.
    Abstract:
    OBJECTIVE: This in vitro study evaluated the effects of a zinc oxide eugenol (ZOE) base on the mechanical properties of a composite resin restoration. METHODS: Class I cavities were prepared on plastic teeth and filled with ZOE plus composite resin, following standard clinical procedures. The samples were sectioned sagittally and the ZOE-resin interface was exposed. After polishing, nanoindentation was performed on the region near the interface, and elastic modulus and hardness were plotted in the form of a color contour map. SEM was employed to observe the interface between composite resin and ZOE base. RESULTS: In the region close to the ZOE base, the elastic modulus and hardness of composite resin reduced to the values of 9.71+/-0.54 and 0.51+/-0.05 GPa, respectively. Eugenol from ZOE had detrimental effects on the composite resin only to a distance of less than 100 microm from the ZOE base. CONCLUSION: Although eugenol suppresses polymerization slightly, by considering the biological advantages of ZOE, together with the results of the current investigation, ZOE may still be considered a suitable base material for composite resin. Bonding is essential for composite resin restorations over ZOE bases to avoid shrinkage detachment.
    [Abstract] [Full Text] [Related] [New Search]