  • Title: Adsorptive properties of albumin, fibrinogen, and gamma-globulin on fluorinated diamond-like carbon films coated on PTFE.
    Author: Ozeki K, Nagashima I, Hirakuri KK, Masuzawa T.
    Journal: J Mater Sci Mater Med; 2010 May; 21(5):1641-8. PubMed ID: 20101441.
    Abstract:
    Fluorinated diamond-like carbon (F-DLC) films were deposited on polytetrafluoroethylene (PTFE) using radio frequency (RF) plasma-enhanced chemical vapor deposition (CVD) by changing the ratio of tetrafluoromethane (CF(4)) and methane (CH(4)). To enhance the adhesion strength of the F-DLC film to the PTFE substrate, the PTFE surface was modified with a N(2) plasma pre-treatment. XPS analysis of the films showed that the C-C bond decreased with increases in the CF(4) ratio, whereas the C-F bond increased with the CF(4) ratio. The F/C ratio of the film also increased with the CF(4) ratio. The pull-out test showed that the adhesion strengths of the films (CF(4)-0-60%) were improved with the plasma pre-treatment. In the film without the plasma pre-treatment, adhesion strength increased with the CF(4) ratio. In contrast, in the case with the plasma pre-treatment, the adhesion strength of the F-DLC film decreased with the increased CF(4) ratio. Regarding the adsorption of albumin, fibrinogen, and gamma-globulin, the amount of adsorbed albumin on the film decreased with an increasing CF(4) ratio, and the amount of adsorbed fibrinogen and gamma-globulin increased with the CF(4) ratio. The CF(4)-0% DLC film showed the most adsorbed albumin and the least adsorbed fibrinogen and gamma-globulin. This indicates that the CF(4)-0% DLC film has higher anti-thrombogenicity than the F-DLC film.
    [Abstract] [Full Text] [Related] [New Search]