  • Title: Development of a ceramic primer with higher bond durability for resin cement.
    Author: Li R.
    Journal: J Oral Rehabil; 2010 Jul; 37(7):560-8. PubMed ID: 20136699.
    Abstract:
    To increase the bond durability of resin to the CAD/CAM ceramic surface, two types of two-bottle type ceramic primers, consisting of Primer A1 or A2 and Primer B, were designed. Primer A1 was prepared by dissolving 25, 50, or 100 mg of gamma-methacryloxypropyltrimethoxysilane in 1 mL of ethanol. Primer A2 was prepared by dissolving 50 mg of mixed silanes, consisting of 1,2-bis(trimethoxysilyl)ethane to gamma-methacryloxypropyltrimethoxysilane, in 1 mL of ethanol. Mole fractions of 1,2-bis(trimethoxysilyl)ethane to gamma-methacryloxypropyltrimethoxysilane were 0, 10, 20, 30, 40 and 50 mol%. Primer B was prepared after dissolving 0.01, 0.05 or 0.1 mol L(-1) hydrochloric acid in ethanol by 50 vol%. Ceramic surface was silanated with a mixture of Primers A1 and B or Primers A2 and B for 1 min, and then air-dried. Commercial GC ceramic primer and Porcelain Liner M were utilized. Thereafter, dual-curing type resin cement was bonded to silanated ceramic surface through visible-light irradiation. Shear bond strength of resin to the ceramic surface was measured, before and after thermo-cycling. Addition of 0.01 or 0.05 mol L(-1) hydrochloric acid to the gamma-methacryloxypropyltrimethoxysilane allowed for significant increases in the bond strength. However, thermo-cycling resulted in significant decreases of approximately 5 MPa in the bond strength. Conversely, when the mixed silane, where 30 mol% of 1,2-bis(trimethoxysilyl)ethane dissolved in gamma-methacryloxypropyltrimethoxysilane, was utilized with 0.05 mol L(-1) hydrochloric acid, the reduction in the bond strength decreased to approximately 2 MPa. The designed ceramic primers exhibited higher ceramic bond durability than commercial ceramic primers.
    [Abstract] [Full Text] [Related] [New Search]