  • Title: Resin composite polyethylene fiber reinforcement: effect on fracture resistance of weakened marginal ridges.
    Author: Ayad MF, Maghrabi AA, García-Godoy F.
    Journal: Am J Dent; 2010 Jun; 23(3):133-6. PubMed ID: 20718208.
    Abstract:
    PURPOSE: To investigate the in vitro effect of polyethylene woven fiber reinforcement of resin composite on the fracture resistance of weakened marginal ridges in molar teeth. METHODS: 50 sound extracted human mandibular molars were used. Specimens were divided into five groups (n = 10). Group 1: served as a control for comparison; Group 2: Class I cavity preparation with resin composite (Prodigy); Group 3: Class I cavity preparation with polyethylene ribbon fiber (Ribbond) and resin composite. Group 4: Class II cavity preparation with resin composite restoration; Group 5: Class II cavity preparation with polyethylene woven fiber and resin composite. Specimens were stored in 100% humidity at 37 degrees C for 7 days. Compressive loading of the teeth was performed with a universal testing machine at a cross-head speed of 0.5 mm/minute until failure. The data were analyzed with 1-way ANOVA followed by the Ryan-Einot-Gabriel-Welsch Multiple Range Test (alpha = 0.05). RESULTS: Reinforcement with polyethylene fiber resulted in significant differences for fracture resistance (P < 0.001). Mean fracture resistance (SD) was [1737.4 (84.8) N] for control group. Among the experimental groups, the highest mean fracture resistance (SD) [1543.8 (71.1) N] was associated with Class I cavity preparation with polyethylene fiber and resin composite. The lowest mean fracture resistance (SD) [869.2 (91.7) N] was recorded for Class II cavity preparation with conventional resin composite.
    [Abstract] [Full Text] [Related] [New Search]