  • Title: Microtensile bond strength of two-step etch-and-rinse adhesive systems on sound and artificial caries-affected dentin.
    Author: Zanchi CH, Lund RG, Perrone LR, Ribeiro GA, del Pino FA, Pinto MB, Demarco FF.
    Journal: Am J Dent; 2010 Jun; 23(3):152-6. PubMed ID: 20718212.
    Abstract:
    PURPOSE: To evaluate the microtensile bond strength of two-step etch-and-rinse adhesive systems on sound and artificial caries-affected dentin (CAD) produced by in vitro monoculture of Streptococcus mutans. METHODS: 10 recently extracted non-carious human third molars were ground to expose a flat dentin surface. Each tooth was sectioned through the long axis with a diamond saw to create two similar halves. One half was used as control (sound dentin - SD) while the other was submitted to caries lesion induction in vitro, using 40 mL of Brain Heart Infusion broth containing 1% sucrose and 40 microL of Streptococcus mutans UA159 inoculum (final bacterial concentration: 1-2 x 105 CFU/mL). The specimens were incubated at 37 degrees C for 4 weeks, and the culture medium was changed every 3 days for 4 weeks. Sound or CAD were alternatively restored as follow (n = 5): Single Bond 2/sound dentin (SB-SD); Single Bond 2/artificial caries-affected dentin (SB-CAD); Prime&Bond NT/sound dentin (PB-SD); and Prime&Bond NT/CAD (PB-CAD).The adhesives were applied to dentin according to manufacturers' instructions, and build-ups of resin composite (Filtek Z250) were prepared and polymerized with a LED light-curing unit (Radii). The restored teeth were stored in distilled water at 37 degrees C for 24 hours and thereafter sectioned perpendicular to the bonded interface with a refrigerated low-speed diamond saw, obtaining three slices per half-tooth (n = 15). The microtensile bond strength (microTBS) test was performed in a universal test machine with a crosshead speed of 1 mm/minute. Bond strengths were calculated in MPa and analyzed by Kruskal-Wallis and Student-Newman-Keuls at a 0.05 level of significance. Failure patterns were examined with an optical microscope. RESULTS: SD produced significantly higher microTBS values than CAD for both adhesive systems. Furthermore, independently of the dentin condition, Single Bond 2 had higher values than Prime Bond NT (P < 0.05). Single Bond 2 showed higher microTBS than Prime Bond NT, in both substrates, and application to CAD reduced the adhesion.
    [Abstract] [Full Text] [Related] [New Search]