  • Title: Multi-temperature synchrotron PXRD and physical properties study of half-Heusler TiCoSb.
    Author: Skovsen I, Bjerg L, Christensen M, Nishibori E, Balke B, Felser C, Iversen BB.
    Journal: Dalton Trans; 2010 Nov 14; 39(42):10154-9. PubMed ID: 20890538.
    Abstract:
    Phase pure samples of the half-Heusler material TiCoSb were synthesised and investigated. Multi-temperature synchrotron powder X-ray diffraction (PXRD) data measured between 90 and 1000 K in atmospheric air confirm the phase purity, but they also reveal a decomposition reaction starting at around 750 K. This affects the high temperature properties since TiCoSb is semiconducting, whereas CoSb is metallic. Between 90 K and 300 K the linear thermal expansion coefficient is estimated to be 10.5 × 10(-6) K(-1), while it is 8.49 10(-6) K(-1) between 550 K and 1000 K. A fit of a Debye model to the Atomic Displacement Parameters obtained from Rietveld refinement of the PXRD data gives a Debye temperature of 395(4) K. The heat capacity was measured between 2 K and 300 K and a Debye temperature of 375(5) K was obtained from modelling of the data. Coming from low temperatures the electrical resistivity shows a metallic to semiconducting transition at 113 K. A relatively high Seebeck coefficient of ∼-250 μV K(-1) was found at 400 K, but the substantial thermal conductivity (∼10 W mK(-1) at 400 K) leads to a moderate thermoelectric figure of merit of 0.025 at 400 K.
    [Abstract] [Full Text] [Related] [New Search]