  • Title: Physical, mechanical, and flexural properties of 3 orthodontic wires: an in-vitro study.
    Author: Juvvadi SR, Kailasam V, Padmanabhan S, Chitharanjan AB.
    Journal: Am J Orthod Dentofacial Orthop; 2010 Nov; 138(5):623-30. PubMed ID: 21055604.
    Abstract:
    INTRODUCTION: Understanding the biologic requirements of orthodontic patients requires proper characterization studies of new archwire alloys. The aims of this study were to evaluate properties of wires made of 2 new materials and to compare their properties with those of stainless steel. METHODS: The sample consisted of 30 straight lengths of 3 types of wires: stainless steel, titanium-molybdenum alloy, and beta-titanium alloy. Eight properties were evaluated: wire dimension, edge bevel, composition, surface characteristics, frictional characteristics, ultimate tensile strength (UTS), modulus of elasticity (E), yield strength (YS), and load deflection characteristics. A toolmaker's microscope was used to measure the edge bevel, and x-ray fluorescence was used for composition analysis. Surface profilometry and scanning electron microscopy were used for surface evaluation. A universal testing machine was used to evaluate frictional characteristics, tensile strength, and 3-point bending. RESULTS: Stainless steel was the smoothest wire; it had the lowest friction and spring-back values and high values for stiffness, E, YS, and UTS. The titanium-molybdenum alloy was the roughest wire; it had high friction and intermediate spring-back, stiffness, and UTS values. The beta-titanium alloy was intermediate for smoothness, friction, and UTS but had the highest spring-back. CONCLUSIONS: The beta-titanium alloy with increased UTS and YS had a low E value, suggesting that it would have greater resistance to fracture, thereby overcoming a major disadvantage of titanium-molybdenum alloy wires. The beta-titanium alloy wire would also deliver gentler forces.
    [Abstract] [Full Text] [Related] [New Search]