  • Title: Method to protect charge recombination in the back-contact dye-sensitized solar cell.
    Author: Yoo B, Kim KJ, Lee DK, Kim K, Ko MJ, Kim YH, Kim WM, Park NG.
    Journal: Opt Express; 2010 Sep 13; 18 Suppl 3():A395-402. PubMed ID: 21165069.
    Abstract:
    We prepared a back-contact dye-sensitized solar cell and investigated effect of the sputter deposited thin TiO₂ film on the back-contact ITO electrode on photovoltaic property. The nanocrystalline TiO₂ layer with thickness of about 11 μm formed on a plain glass substrate in the back-contact structure showed higher optical transmittance than that formed on an ITO-coated glass substrate, which led to an improved photocurrent density by about 6.3%. However, photovoltage was found to decrease from 817 mV to 773 mV. The photovoltage recovered after deposition of a 35 nm-thick thin TiO₂ film on the surface of the back-contact ITO electrode. Little difference in time constant for electron transport was found for the back-contact ITO electrodes with and without the sputter deposited thin TiO₂ film. Whereas, time constant for charge recombination increased after introduction of the thin TiO₂ film, indicating that such a thin TiO₂ film protected back electron transfer, associated with the recovery of photovoltage. As the result of the improved photocurrent density without deterioration of photovoltage, the back-contact dye-sensitized solar cell exhibited 13.6% higher efficiency than the ITO-coated glass substrate-based dye-sensitized solar cell.
    [Abstract] [Full Text] [Related] [New Search]