  • Title: Synthesis and photo-degradation application of WO3/TiO2 hollow spheres.
    Author: Lv K, Li J, Qing X, Li W, Chen Q.
    Journal: J Hazard Mater; 2011 May 15; 189(1-2):329-35. PubMed ID: 21398030.
    Abstract:
    A WO(3)/TiO(2) composite, hollow-sphere photocatalyst with average diameter of 320 nm and shell thickness of 50 nm was successfully prepared using a template method. UV-vis diffuse reflectance spectra illustrated that the main absorption edges of the WO(3)/TiO(2) hollow spheres were red-shifted compared to the TiO(2) hollow spheres, indicating an extension of light absorption into the visible region of the composite photocatalyst. The WO(3) and TiO(2) phases were confirmed by X-ray diffraction analysis. BET isotherms revealed that the specific surface area and average pore diameter of the hollow spheres were 40.95 m(2)/g and 19 nm, respectively. Photocatalytic experiments indicate that 78% MB was degraded by WO(3)/TiO(2) hollow spheres under visible light within 80 min. Under the same conditions, only 24% MB can be photodegraded by TiO(2). The photocatalytic mineralization of MB, catalyzed by TiO(2) and WO(3)/TiO(2), proceeded at a significantly higher rate under UV irradiation than that under visible light, and more significant was the increase in the apparent rate constant with the WO(3)/TiO(2) composite semiconductor material which was 3.2- and 3.5-fold higher than with the TiO(2) material under both UV and visible light irradiation. The increased photocatalytic activity of the coupled nanocomposites was attributed to photoelectron/hole separation efficiency and the extension of the wavelength range of photoexcitation.
    [Abstract] [Full Text] [Related] [New Search]