  • Title: Preparation, characterization and photoluminescence properties of BaB2O4: Eu3+ red phosphor.
    Author: Liu J, Wang XD, Wu ZC, Kuang SP.
    Journal: Spectrochim Acta A Mol Biomol Spectrosc; 2011 Sep; 79(5):1520-3. PubMed ID: 21658993.
    Abstract:
    A new red emitting BaB2O4: Eu3+ phosphor was synthesized by solid-state reaction method. X-ray powder diffraction (XRD) analysis confirmed the monoclinic formation of BaB2O4. Field-emission scanning electron-microscopy (FE-SEM) observation indicated that the microstructure of the phosphor consisted of irregular grains with heavy agglomerate phenomena. Upon excitation with 394 nm light, the BaB2O4: Eu3+ phosphor shows bright red emissions with the highest photoluminescence (PL) intensity at 611 nm due to 5D0→7F2 transitions of Eu3+ ions. The CIE chromaticity coordinates are calculated from the emission spectrum to be x=0.64, y=0.35. The effects of the Eu3+ concentration on the PL were investigated. The results showed that the optimum concentration of Eu3+ in BaB2O4 host is 6 mol% and the dipole-dipole interaction plays the major role in the mechanism of concentration quenching of Eu3+ in BaB2O4: Eu3+ phosphor. The effect of charge compensation on the emission intensity was also studied. The charge compensations of Li+, Na+ and K+ anions all increased the luminescent intensity of BaB2O4: Eu3+. K+ anion gave the best improvement to enhance the intensity of the emission, indicating K+ is the optimal charge compensator. All properties show that this phosphor could serve as a potential candidate for application as a red phosphor for NUV chip LED.
    [Abstract] [Full Text] [Related] [New Search]