  • Title: Elemental distribution and thermoelectric properties of layered tellurides 39R-M(0.067)Sb(0.667)Te(0.266) (M=Ge, Sn).
    Author: Schneider MN, Fahrnbauer F, Rosenthal T, Döblinger M, Stiewe C, Oeckler O.
    Journal: Chemistry; 2012 Jan 23; 18(4):1209-18. PubMed ID: 22213207.
    Abstract:
    The isostructural phases 39R-Ge(0.067)Sb(0.667)Te(0.266) (R3m, a=4.2649(1), c=75.061(2) Å) and 39R-Sn(0.067)Sb(0.667)Te(0.266) (R3m, a=4.2959(1), c=75.392(2) Å) were prepared by quenching stoichiometric melts of the pure elements and subsequent annealing at moderate temperatures. Their structures are comparable to "superlattices" synthesized by layer-by-layer deposition onto a substrate. These structures show no stacking disorder by electron microscopy. The structure of the metastable layered phases are similar to that of 39R-Sb(10)Te(3) (equivalent to Sb(0.769)Te(0.231)), which contains four A7 gray-arsenic-type layers of antimony alternating with Sb(2)Te(3) slabs. Joint refinements on single-crystal diffraction data using synchrotron radiation at several K edges were performed to enhance the scattering contrast. These refinements show that the elemental distributions at some atom positions are disordered whereas otherwise the structures are long-range ordered. The variation of the elemental concentration correlates with the variation in interatomic distance. Z-contrast scanning transmission electron microscopy (HAADF-STEM) on 39R-Ge(0.067)Sb(0.667)Te(0.266) confirms the presence of concentration gradients. The carrier-type of the isostructural metal (A7-type lamellae)-semiconductor heterostructures (Ge/Sn-doped Sb(2)Te(3) slabs) varies from n-type (Ge(0.067)Sb(0.667)Te(0.266)) to p-type (Sn(0.067)Sb(0.667)Te(0.266)). Although the absolute values of the Seebeck coefficient reached about 50-70 μV/K and the electrical conductivity is relatively high, the two isotypic phases exhibit a maximal thermoelectric figure of merit (ZT) of 0.06 at 400 °C as their thermal conductivity (κ≈8-9.5 W/mK at 400 °C) lies interestingly in between that of antimony and pure Sb(2)Te(3).
    [Abstract] [Full Text] [Related] [New Search]