  • Title: Biocompatibility and resorption of a radiopaque premixed calcium phosphate cement.
    Author: Aberg J, Henriksson HB, Engqvist H, Palmquist A, Brantsing C, Lindahl A, Thomsen P, Brisby H.
    Journal: J Biomed Mater Res A; 2012 May; 100(5):1269-78. PubMed ID: 22359393.
    Abstract:
    Calcium phosphate cements (CPC) are used as bone void filler in various orthopedic indications; however, there are some major drawbacks regarding mixing, transfer, and injection of traditional CPC. By using glycerol as mixing liquid, a premixed calcium phosphate cement (pCPC), some of these difficulties can be overcome. In the treatment of vertebral fractures the handling characteristics need to be excellent including a high radio-opacity for optimal control during injection. The aim of this study is to evaluate a radiopaque pCPC regarding its resorption behavior and biocompatibility in vivo. pCPC and a water-based CPC were injected into a Ø 4-mm drilled femur defect in rabbits. The rabbits were sacrificed after 2 and 12 weeks. Cross sections of the defects were evaluated using histology, electron microscopy, and immunohistochemical analysis. Signs of inflammation were evaluated both locally and systemically. The results showed a higher bone formation in the pCPC compared to the water-based CPC after 2 weeks by expression of RUNX-2. After 12 weeks most of the cement had been resorbed in both groups. Both materials were considered to have a high biocompatibility since no marked immunological response was induced and extensive bone ingrowth was observed. The conclusion from the study was that pCPC with ZrO(2) radiopacifier is a promising alternative regarding bone replacement material and may be suggested for treatment of, for example, vertebral fractures based on its high biocompatibility, fast bone ingrowth, and good handling properties.
    [Abstract] [Full Text] [Related] [New Search]