  • Title: Dispersion polymerization of styrene using a polystyrene/poly(L-glutamic acid) block copolymer as a stabilizer.
    Author: Itoh T, Komada S, Ihara E, Inoue K.
    Journal: J Colloid Interface Sci; 2012 Dec 15; 388(1):112-7. PubMed ID: 22999462.
    Abstract:
    A block copolymer (PS-b-poly(L-Glu)) composed of polystyrene and poly(l-glutamic acid) was used as a stabilizer for dispersion polymerization of styrene. When dispersion polymerization of styrene was conducted at 70°C in 80% dimethylformamide-water with 0.5 wt% PS-b-poly(L-Glu), spherical polystyrene particles with D(n)=0.72 μm and narrow size distribution were obtained. Whereas AIBN concentration did not have any effects on particle size, molecular weight of the polystyrene particles was strongly dependent on the initiator concentration. As concentration of the PS-b-poly(L-Glu) increased from 0.2 to 1.0 wt%, particle size decreased from D(n)=0.91 to 0.69 μm with keeping surface area occupied by one poly(L-glutamic acid) chain about S=50 nm(2). On the other hand, an increase in initial concentration of styrene from 2 to 20 wt% caused an increase in particle size from D(n)=0.48 to 1.36 μm and a decrease in surface area per poly(L-glutamic acid) block from S=91 to 45 nm(2). Colloidal stability of the polystyrene particles in aqueous solution was responsive to pH due to the surface-grafted poly(L-glutamic acid). For dispersion polymerization of styrene, the PS-b-poly(L-Glu) functions as both a stabilizer and a surface modifier.
    [Abstract] [Full Text] [Related] [New Search]