  • Title: Continuous equilibrated growth of ordered block copolymer thin films by electrospray deposition.
    Author: Hu H, Rangou S, Kim M, Gopalan P, Filiz V, Avgeropoulos A, Osuji CO.
    Journal: ACS Nano; 2013 Apr 23; 7(4):2960-70. PubMed ID: 23451911.
    Abstract:
    Deposition of block copolymer thin films is most often accomplished in a serial process where material is spin coated onto a substrate and subsequently annealed, either thermally or by solvent vapor, to produce a well-ordered morphology. Here we show that under appropriate conditions, well-ordered block copolymer films may be continuously grown under substrate equilibrated conditions by slow deposition of discrete subattoliter quantities of material using electrospray. We conduct time-resolved observations and investigate the effects of process parameters that underpin film morphology including solvent selectivity, substrate temperature, block-substrate selectivity, and flow rate of the feed solution. For a PEO cylinder-forming poly(styrene-b-ethylene oxide) block copolymer, we uncover a wide temperature window from 90 to 150 °C and an ideal flow rate of 2 μL/min for ordered film deposition from dilute acetone solutions. PEO cylinders aligned with their long axes perpendicular to the film-air interface at optimal spray conditions. Using poly(styrene-b-methyl methacrylate) deposited onto neutrally selective surfaces, we show that the substrate-equilibrated process results in vertically oriented microdomains throughout the film, indicating a preservation of the initial substrate-dictated morphology during the film deposition. Electrospray offers a new and potentially exciting route for controlled, continuous growth of block copolymer thin films and manipulation of their microstructure.
    [Abstract] [Full Text] [Related] [New Search]