  • Title: A novel and easy-to-prepare strontium(II) modified calcium phosphate bone cement with enhanced mechanical properties.
    Author: Schumacher M, Henß A, Rohnke M, Gelinsky M.
    Journal: Acta Biomater; 2013 Jul; 9(7):7536-44. PubMed ID: 23523939.
    Abstract:
    The aim of this study was to evaluate two different approaches to obtaining strontium-modified calcium phosphate bone cements (SrCPCs) without elaborate synthesis of Sr-containing calcium phosphate species as cement precursors that could release biologically effective doses of Sr(2+) and thus could improve the healing of osteoporotic bone defects. Using strontium carbonate as a strontium(II) source, it was introduced into a hydroxyapatite-forming cement either by the addition of SrCO3 to an α-tricalcium phosphate-based cement precursor mixture (A-type) or by substitution of CaCO3 by SrCO3 during precursor composition (S-type). The cements, obtained after setting in a water-saturated atmosphere, contained up to 2.2at.% strontium in different distribution patterns as determined by time-of-flight secondary ion mass spectrometry and energy-dispersive X-ray spectroscopy. The setting time of CPC and A-type cements was in the range of 6.5-7.5min and increased for substitution-type cements (12.5-13.0min). Set cements had an open porosity between 26 and 42%. Compressive strength was found to increase from 29MPa up to 90% in substituted S-type cements (58MPa). SrCPC samples released between 0.45 and 1.53mgg(-1) Sr(2+) within 21days and showed increased radiopacity. Based on these findings, the SrCPC developed in this study could be beneficial for the treatment of defects of systemically impaired (e.g. osteoporotic) bone.
    [Abstract] [Full Text] [Related] [New Search]