  • Title: In-vitro strength degradation of dental ceramics and novel PICN material by sharp indentation.
    Author: Coldea A, Swain MV, Thiel N.
    Journal: J Mech Behav Biomed Mater; 2013 Oct; 26():34-42. PubMed ID: 23807311.
    Abstract:
    OBJECTIVES: To determine the flexural strength and subsequent strength degradation of a range of dental CAD/CAM ceramic materials and novel PICN (Polymer-Infiltrated-Ceramic-Network) materials by means of pre-damaging with Vickers indentations at various loads. METHODS: The materials tested included (Mark II, PICN test material 1 and 2, In-Ceram Alumina, VM 9, In-Ceram YZ; Vita Zahnfabrik, Bad Saeckingen, Germany) and (IPS e.max CAD, Ivoclar Vivadent, Schaan, Liechtenstein). Bending bars were cut and lapped with 15 µm diamond suspension. Initial flexural strength (n=10) was determined in three-point-bending. To evaluate the damage tolerance, Vickers indentations were placed on the bending bars (n=35) with varying loads (1.96-98.07 N). The indented bending bars were subsequently loaded to fracture in three-point-bending. In addition, the fracture toughness was determined by the indentation strength (IS) and the SEVNB technique (n=5). RESULTS: With increasing indentation loads the fracture strength of all materials tested decreased. The material with the highest fracture resistance to indentation induced damage, was the PICN test material 1 with an indentation load-flexural strength curve slope of 0.21. In-Ceram YZ exhibited the highest damage susceptibility with a slope of 0.4. The fracture toughness varied with the measurement technique and material in the range of 0.82 (VM 9) to 4.94 (In-Ceram YZ) MPa√m for the SEVNB method and 0.96 (VM 9) to 4.97 (In-Ceram YZ) MPa√m for the IS method respectively. SIGNIFICANCE: This study aims to indicate the likely clinical behavior by evaluating the damage tolerance and R-curve behavior of dental ceramics by in-vitro strength degradation and fracture toughness measurements.
    [Abstract] [Full Text] [Related] [New Search]