  • Title: Assembling and redispersibility of rice straw nanocellulose: effect of tert-butanol.
    Author: Jiang F, Hsieh YL.
    Journal: ACS Appl Mater Interfaces; 2014 Nov 26; 6(22):20075-84. PubMed ID: 25341690.
    Abstract:
    Self-assembling of sulfuric-acid-hydrolyzed cellulose nanocrystals (CNCs, 6.4 nm wide) and TEMPO oxidized cellulose nanofibrils (CNFs, 2.1 nm wide) from aqueous suspensions was induced by rapid freezing (-196 °C, 10 min) and slow lyophilization (-50 °C, 0.05 mbar, 2 days). The assembled structures contain submicron (200-700 nm) wide and tens of micrometer long fibers at up to 0.1-0.5% and 0.01-0.05%, the critical fiber-to-film transformation concentrations for CNCs and CNFs, respectively. The assembled fiber widths were significantly reduced to ∼40 nm, that is, by 1 order of magnitude, when 10% of the aqueous media was replaced with tert-butanol. Further increasing tert-butanol contents in the media to 93/7 (CNCs) and 50/50 (CNFs) tert-butanol/water, both at 0.1% nanocellulose concentration, reduced longitudinal assembling for CNCs and lateral assembling for CNFs as well as increased critical fiber-to-film transformation concentration for CNFs. While all assembled structure could be redispersed in water, those from tert-butanol/water could also be easily redispersed in DMF aided with brief 2 min ultrasonication. None of the assembled structures could be redispersed in the lower dielectric constant ethanol, acetone or chloroform.
    [Abstract] [Full Text] [Related] [New Search]