  • Title: Designing new biocompatible glass-forming Ti75-x Zr10 Nbx Si15 (x = 0, 15) alloys: corrosion, passivity, and apatite formation.
    Author: Abdi S, Oswald S, Gostin PF, Helth A, Sort J, Baró MD, Calin M, Schultz L, Eckert J, Gebert A.
    Journal: J Biomed Mater Res B Appl Biomater; 2016 Jan; 104(1):27-38. PubMed ID: 25611821.
    Abstract:
    Glass-forming Ti-based alloys are considered as potential new materials for implant applications. Ti75 Zr10 Si15 and Ti60 Zr10 Nb15 Si15 alloys (free of cytotoxic elements) can be produced as melt-spun ribbons with glassy matrix and embedded single β-type nanocrystals. The corrosion and passivation behavior of these alloys in their homogenized melt-spun states have been investigated in Ringer solution at 37°C in comparison to their cast multiphase crystalline counterparts and to cp-Ti and β-type Ti-40Nb. All tested materials showed very low corrosion rates as expressed in corrosion current densities icorr  < 50 nA/cm(2). Electrochemical and surface analytical studies revealed a high stability of the new alloys passive states in a wide potential range. This corresponds to low passive current densities ipass  = 2 ± 1 µA/cm(2) based on the growth of oxide films with thickness d <10 nm. A homogeneous constituent distribution in the melt-spun alloys is beneficial for stable surface passivity. The addition of Nb does not only improve the glass-forming ability and the mechanical properties but also supports a high pitting resistance even at extreme anodic polarization up to 4V versus SCE were oxide thickness values of d ∼35 nm are reached. With regard to the corrosion properties, the Nb-containing nearly single-phase glassy alloy can compete with the β-type Ti-40Nb alloy. SBF tests confirmed the ability for formation of hydroxyapatite on the melt-spun alloy surfaces. All these properties recommend the new glass-forming alloys for application as wear- and corrosion-resistant coating materials for implants.