  • Title: Effect of Smear Layers Created by Different Burs on Durability of Self-Etching Adhesive Bond to Dentin of Primary Teeth.
    Author: Rirattanapong P, Senawongse P, Harnirattisal C, Wunsiw W.
    Journal: J Clin Pediatr Dent; 2015; 39(3):224-30. PubMed ID: 26208066.
    Abstract:
    AIM: The aim of this study was to evaluate the effects of a smear layer generated by a high-speed diamond or carbide bur on the durability of microtensile bond strength (μTBS) of a self-etching adhesive to primary dentin. STUDY DESIGN: Flat occlusal dentin surfaces of 105 human primary molars were exposed using 600 grit silicon carbide paper before being divided into 2 groups for further grinding with either a highspeed diamond or carbide bur. Ten prepared dentin surfaces treated by each bur were evaluated for the characteristics of the smear layer using a scanning electron microscope (SEM). Seventy-five specimens from each bur-prepared group were applied with a 2-step self-etching adhesive (Clearfil SE Bond(®)) then built up with a resin composite. Each bonded specimen was sectioned into a 1-mm thick slab and trimmed to a dumbbell shape with a cross-sectional area of approximately 1 mm(2). All slabs were divided into 3 groups (n=25) according to 3 storage times of 24 hrs, 3 months, and 6 months, in distilled water at 37°C. After storage, the μTBS was determined using a universal testing machine. All fracture specimens were prepared for observation of failure modes. Ten bonded specimens of each bur group were prepared for observation of the resin-dentin interface using an SEM. Smear-layer thickness, μTBS, and failure mode distributions were statistically analyzed. RESULTS: The high speed carbide bur created a significantly thinner smear layer than the diamond bur (p < 0.05). Dentin surfaces treated with a high-speed carbide bur generally obtained significantly higher μTBS than the diamond bur group (p < 0.05). The μTBS gradually decreased over time such that specimens stored for 6 months had significantly lower bond strength than those stored for 24 hrs (p < 0.05). Self-etching adhesive created a hybrid layer of the same thickness when prepared with either a carbide bur or diamond bur, but the carbide bur group had longer and more resin tags. CONCLUSION: Highspeed carbide bur groups had a higher μTBS than diamond bur groups for all storage times, and bond strengths decreased over time in both substrate groups. The use of a carbide bur produced a thinner smear layer and therefore is recommended when using this 2-step self-etching adhesive to bond the resin composite to primary dentin.
    [Abstract] [Full Text] [Related] [New Search]