  • Title: Effect of Different Surface Treatments on the Bond Strength of Lithium Disilicate Ceramic to the Zirconia Core.
    Author: Yilmaz-Savas T, Demir N, Ozturk AN, Kilic HS.
    Journal: Photomed Laser Surg; 2016 Jun; 34(6):236-43. PubMed ID: 27096900.
    Abstract:
    OBJECTIVE: The aim of this study was to evaluate the effect of different surface treatments [sandblasting, Erbium:Yttrium-Aluminium-Garnet (Er:YAG), and femtosecond lasers] on the shear bond strength (SBS) of the CAD-on technique. BACKGROUND DATA: Although demand for all-ceramic restorations has increased, chipping remains one of the major problems for zirconia-based restorations. MATERIALS AND METHODS: Forty yttrium-stabilized tetragonal zirconia polycrystalline (Y-TZP) zirconia plates (IPS e.max ZirCAD, Ivoclar Vivadent) were cut, sintered (12.4 × 11.4 × 3 mm) and divided into four groups according to the surface treatments (n = 10): a control group with no surface treatment (Group C), sandblasting with 50 μm Al2O3 (Group S), Er:YAG laser irradiation (Group E), and femtosecond laser irradiation (Group F). Also, 40 cylindrical (5 mm diameter, 2 mm height) lithium disilicate (IPS e.max CAD) veneer ceramics were cut and fused to all zirconia cores by a glass-fusion ceramic and crystallized according to the CAD-on technique. Specimens were subjected to shear force using a universal testing machine. The load was applied at a crosshead speed of 0.5 mm/min until failure. Mean SBS (MPa) were analyzed with one way ANOVA (p < 0.05). The failed specimens were examined under a stereomicroscope at ×20 to classify the mode of failure. RESULTS: The highest SBS was observed in Group F (36 ± 3.31 MPa), followed by Group S (33.03 ± 5.05 MPa), and Group C (32.52 ± 10.15 MPa). The lowest SBS was observed in Group E (31.02 ± 4.96 MPa), but no significant differences were found between the control and surface treated groups (p = 0.377). All the specimens showed a mixed type of failure. CONCLUSIONS: Femtosecond laser application increased the bond strength between zirconia-veneer specimens. However, the novel CAD-on technique with no surface treatment also showed high bonding strength. Thus, this technique could prevent ceramic chipping without additional surface treatments.
    [Abstract] [Full Text] [Related] [New Search]