  • Title: Effect of silane contamination on dentin bond strength.
    Author: Chen L, Hammond BD, Alex G, Suh BI.
    Journal: J Prosthet Dent; 2017 Mar; 117(3):438-443. PubMed ID: 27692582.
    Abstract:
    STATEMENT OF PROBLEM: Intraoral repair of porcelain or other silica-based ceramics typically requires the use of silane in the repair protocol. Some porcelain intraoral repairs also involve bonding to exposed or involved tooth tissues including dentin. A study is needed to evaluate whether the cross-contamination of dentin with silane affects bond strength to this tissue. PURPOSE: The purpose of this in vitro study was to investigate the effect of silane cross-contamination on dentin bond strength. MATERIAL AND METHODS: Flat surfaces of human dentin specimens were created, followed by wet polishing with 320-grit silicon carbide paper. The dentin specimens were divided into 4 groups: group SE (All-Bond Universal Adhesive used in self-etching mode); group SiSE (silane applied to dentin followed by All-Bond Universal Adhesive used in self-etching mode); group ER (All-Bond Universal Adhesive used in total-etch (etch-and-rinse) mode); and group ERSi (Etch and rinse and silane applied to dentin followed by All-Bond Universal Adhesive). The dentin specimens were treated with a universal adhesive (All-Bond Universal) and bonded with a composite resin, using an Ultradent jig mold. Shear bond strength (n=10) was measured after 24 hours of water storage at 37°C. After the shear bond strength test, the dentin sides of fractured specimens in each group were examined with a stereomicroscope at ×15 magnification to determine failure modes. Data were statistically analyzed by 2-way and a 1-way ANOVA followed by post hoc Tukey honest significant difference test (α=.05). Scanning electron microscopy examination was used to evaluate the dentin surface morphology before and after bonding. RESULTS: The shear bond strength of composite resin to dentin was not affected adversely when the dentin was contaminated with silane prior to using All-Bond Universal in the self-etch or total- etch (phosphoric acid) mode. SE, 30.3 ±3.8 MPa; SiSE, 32.9 ±3.9 MPa; ER, 34.9 ±3.1 MPa; ERSi: 35.2 ±4.9 MPa (P>.05) CONCLUSIONS: Under the conditions of this study, cross-contamination of dentin with silane before the use of All-Bond Universal in the self-etch or total-etch with phosphoric acid mode did not adversely affect composite resin bond strength to dentin.
    [Abstract] [Full Text] [Related] [New Search]