  • Title: Filler Content, Surface Microhardness, and Rheological Properties of Various Flowable Resin Composites.
    Author: Jager S, Balthazard R, Dahoun A, Mortier E.
    Journal: Oper Dent; 2016; 41(6):655-665. PubMed ID: 27820692.
    Abstract:
    OBJECTIVES: The objectives of this study were to determine the filler content, the surface microhardness (at baseline and after immersion in water for 2 years), and the rheological properties of various flowable resin composites. METHODS: Three flowable resin composites (Grandioso Heavy Flow [GHF], Grandio Flow [GRF], Filtek Supreme XTE Flow [XTE]), one pit and fissure sealant resin composite (ClinPro [CLI]), and three experimental flowable resin composites with the same matrix and a variable filler content (EXPA, EXPB, EXPC) were tested. The filler content was determined by calcination. The Vickers surface microhardness was determined after polymerization and then after immersion in distilled water at 37°C for 7, 60, 180, 360, and 720 days. The rheological measurements were performed using a dynamic shear rheometer. RESULTS: The determined filler contents differed from the manufacturers' data for all the materials. The materials with the highest filler content presented the highest microhardness, but filler content did not appear to be the only influencing parameter. With respect to the values recorded after photopolymerization, the values were maintained or increased after 720 days compared with the initial microhardness values, except for GHF. For the values measured after immersion for 7 days, an increase in microhardness was observed for all the materials over time. All the materials were non-Newtonian, with shear-thinning behavior. At all the shear speeds, GRF presented a lower viscosity to GHF and XTE. CONCLUSIONS: GRF presented a low viscosity before photopolymerization, associated with high filler content, thereby providing a good compromise between spreadability and mechanical properties after photopolymerization.
    [Abstract] [Full Text] [Related] [New Search]