  • Title: Enhancing the in vitro anticancer activity of albendazole incorporated into chitosan-coated PLGA nanoparticles.
    Author: Kang BS, Choi JS, Lee SE, Lee JK, Kim TH, Jang WS, Tunsirikongkon A, Kim JK, Park JS.
    Journal: Carbohydr Polym; 2017 Mar 01; 159():39-47. PubMed ID: 28038752.
    Abstract:
    To improve the solubility and anticancer activity of albendazole (ABZ), chitosan (CS)-coated poly-dl-lactic-co-glycolic acid (PLGA) nanoparticles were developed. CS was used to coat ABZ-loaded PLGA nanoparticles to enhance both mucoadhesiveness and colloidal stability. CS-coated PLGA nanoparticles were prepared by suspending the nanoparticles in CS solution after solvent diffusion. The CS-coated PLGA nanoparticles were characterized, and ABZ release was studied in vitro from various formulations. The mucoadhesive properties and in vitro anticancer activities of CS-coated PLGA nanoparticles were investigated by measurement of zeta potentials and the MTT assay, respectively. Spherical nanoparticles below 500nm in diameter were successfully prepared; the particle size distribution was narrow. Complete encapsulation of ABZ in CS-coated PLGA nanoparticles was confirmed by SEM, FTIR, DSC, and XRD. The particle sizes of CS-coated PLGA nanoparticles were in the range of 260-480nm; the encapsulation efficiency was 43.4-54.6%; and the yield 58.5-67.8%. The zeta potential of CS-coated nanoparticles was above +27mV and stability was maintained for 4 weeks. At pH 7.4, the in vitro release of ABZ from nanoparticles (P188-5) was 200-fold higher than that from untreated ABZ; this persisted for 12h. Moreover, ABZ release from CS-coated PLGA nanoparticles (P188-CS0.5) was 1.5-fold higher than that from untreated ABZ at pH 1.2. Additionally, the ABZ-loaded CS-coated nanoparticles exhibited superior mucoadhesion and improved cytotoxicity. The results show that CS coating of PLGA nanoparticles may improve the anticancer effect and the mucoadhesive properties of ABZ-loaded nanoparticles.
    [Abstract] [Full Text] [Related] [New Search]