  • Title: Optimizing the photochemical conversion of UV-vis light of silver-nanoparticles decorated TiO2 nanotubes based photoanodes.
    Author: Gaidi M, Trabelsi K, Hajjaji A, Chourou ML, Alhazaa AN, Bessais B, El Khakani MA.
    Journal: Nanotechnology; 2018 Jan 05; 29(1):015703. PubMed ID: 29082898.
    Abstract:
    Homogeneous decoration of TiO2 nanotubes (NTs) by Ag metallic nanoparticles (NPs) was carried out by a relatively simple photoreduction process. This Ag-NPs decoration was found to improve the photoconversion efficiency of the TiO2-NTs based photoanodes. The x-ray photoelectron spectroscopy and x-ray diffraction analyses confirmed that all the Ag-NPs are metallic and the underlying TiO2-NTs crystallize in the anatase phase after their annealing at 400 °C, respectively. Transmission electron microscopy observations have confirmed the effective decoration of the TiO2-NTs' surface by Ag-NPs, and allowed to measure the average Ag-NPs size, which was found to increase linearly from (4 ± 2) nm to (16 ± 4) nm when the photoreduction time is increased from 5 to 20 min. The diffuse reflectivity of the Ag-NPs decorated TiO2-NTs was found to decrease significantly as compared to the undecorated TiO2-NTs. Interestingly, the Ag-NPs decorated TiO2-NTs exhibited a significantly enhanced photochemical response, under visible radiation, with regards to the undecorated NTs. This enhancement was found to reach its maximum for the TiO2-NTs decorated with Ag-NPs having the optimal average diameter of ∼8.5 nm. The maximum photoconversion efficiency of Ag-NPs decorated TiO2-NTs was about two times greater than for the undecorated ones. This improved photo-electro-chemical response is believed to be associated with the additional absorption of visible light of Ag-NPs through the localized surface plasmon resonance phenomenon. This interpretation is supported by the fact that the photoluminescence intensity of the Ag-NPs decorated TiO2-NTs was found to decrease significantly as compared to undecorated NTs, due to charge carriers trapping in the Ag NPs. This demonstrates that Ag-NPs decoration promotes photogenerated charges separation in the TiO2-NTs, increasing thereby their capacity for current photogeneration. The surface decoration of TiO2 NTs by noble metals NPs is expected to impact positively the use of TiO2-NTs based photoanodes in some energetic applications such as hydrogen generation and photo-electrochemical solar cells.
    [Abstract] [Full Text] [Related] [New Search]