  • Title: Correlations between fracture load of zirconia implant supported single crowns and mechanical properties of restorative material and cement.
    Author: Rohr N, Märtin S, Fischer J.
    Journal: Dent Mater J; 2018 Mar 30; 37(2):222-228. PubMed ID: 29176305.
    Abstract:
    Zirconia implants that were restored with veneered zirconia displayed severe chipping rates of the restorations in clinical studies. Purpose of this study was to evaluate the fracture load of different zirconia implant supported monolithic crown materials (zirconia, alumina, lithium disilicate, feldspar ceramic and polymer-infiltrated ceramic) cemented with various cements (Harvard LuteCem SE, Harvard Implant Semi-permanent, Multilink Automix, VITA Adiva F-Cem). Flexural strength and fracture toughness of crown materials and compressive strength of the cements were measured. Fracture load values of crowns fabricated from lithium disilicate, feldspar ceramic and polymer-infiltrated ceramic were increased when cement with high compressive strength was used. Fracture loads for zirconia and alumina crowns were not influenced by the cement. Flexural strength and fracture toughness of the ceramics correlated linearly with the respective fracture load when using adhesive cement with high compressive strength. To achieve sufficient fracture load values, cementation with adhesive cement is essential for feldspar and polymer-infiltrated ceramic.
    [Abstract] [Full Text] [Related] [New Search]