  • Title: Effect of Thickness on Light Transmission and Vickers Hardness of Five Bulk-fill Resin-based Composites Using Polywave and Single-peak Light-emitting Diode Curing Lights.
    Author: Maghaireh GA, Price RB, Abdo N, Taha NA, Alzraikat H.
    Journal: Oper Dent; 2019; 44(1):96-107. PubMed ID: 29953339.
    Abstract:
    OBJECTIVES:: This study compared light transmission through different thicknesses of bulk-fill resin-based composites (RBCs) using a polywave and a single-peak light-emitting diode light-curing unit (LCU). The effect on the surface hardness was also evaluated. METHODS:: Five bulk-fill RBCs were tested. Specimens (n=5) of 1-, 2-, 4-, or 6-mm thickness were photopolymerized for 10 seconds from the top using a polywave (Bluephase Style) or single-peak (Elipar S10) LCU, while a spectrophotometer monitored in real time the transmitted irradiance and radiant exposure reaching the bottom of the specimen. After 24 hours of storage in distilled water at 37°C, the Vickers microhardness (VH) was measured at top and bottom. Results were analyzed using multiple-way analysis of variance, Tukey post hoc tests, and multivariate analysis (α=0.05). RESULTS:: The choice of LCU had no significant effect on the total amount of light transmitted through the five bulk-fill RBCs at each thickness. There was a significant decrease in the amount of light transmitted as the thickness increased for all RBCs tested with both LCUs ( p<0.001). Effect of LCU on VH was minimal (ηp2=0.010). The 1-, 2-, and 4-mm-thick specimens of SDR, X-tra Fill, and Filtek Bulk Restorative achieved a VHbottom/top ratio of approximately 80% when either LCU was used. CONCLUSIONS:: The total amount of light transmitted through the five bulk-fill RBCs was similar at the different thicknesses using either LCU. The polywave LCU used in this study did not enhance the polymerization of the tested bulk-fill RBCs when compared with the single-peak LCU.
    [Abstract] [Full Text] [Related] [New Search]