  • Title: High-Performance All-Solid-State Polymer Electrolyte with Controllable Conductivity Pathway Formed by Self-Assembly of Reactive Discogen and Immobilized via a Facile Photopolymerization for a Lithium-Ion Battery.
    Author: Wang S, Liu X, Wang A, Wang Z, Chen J, Zeng Q, Jiang X, Zhou H, Zhang L.
    Journal: ACS Appl Mater Interfaces; 2018 Aug 01; 10(30):25273-25284. PubMed ID: 29975039.
    Abstract:
    All-solid-state polymer electrolytes (SPEs) have aroused great interests as one of the most promising alternatives for liquid electrolyte in the next-generation high-safety, and flexible lithium-ion batteries. However, some disadvantages of SPEs such as inefficient ion transmission capacity and poor interface stability result in unsatisfactory cyclic performance of the assembled batteries. Especially, the solid cell is hard to be run at room temperature. Herein, a novel and flexible discotic liquid-crystal (DLC)-based cross-linked solid polymer electrolyte (DLCCSPE) with controlled ion-conducting channels is fabricated via a one-pot photopolymerization of oriented reactive discogen, poly(ethylene glycol)diacrylate, and lithium salt. The experimental results indicate that the macroscopic alignment of self-assembled columns in the DLCCSPEs is successfully obtained under annealing and effectively immobilized via the UV photopolymerization. Because of the existence of unique oriented structure in the electrolytes, the prepared DLCCSPE films exhibit higher ionic conductivities and better comprehensive electrochemical properties than the DLCCSPEs without controlled ion-conductive pathways. Especially, the assembled LiFePO4/Li cells with oriented electrolyte show an initial discharge capacity of 164 mA h g-1 at 0.1 C and average specific discharge capacities of 143, 135, and 149 mA h g-1 at the C-rates of 0.5, 1, and 0.2 C, respectively. In addition, the solid cell also shows the first discharge capacity of 124 mA h g-1 (0.2 C) at room temperature. The outstanding cell performance of the oriented DLCCSPE should be originated from the macroscopically oriented and self-assembled DLC, which can form ion-conducting channels. Thus, combining the excellent performance of DLCCSPE and the simple one-pot fabricating process of the DLC-based all-solid-state electrolyte, it is believed that the DLC-based electrolyte can be one of the most promising electrolyte materials for the next-generation high-safety solid lithium-ion batteries.