  • Title: Hydrofluoric acid concentrations: Effect on the cyclic load-to-failure of machined lithium disilicate restorations.
    Author: Prochnow C, Venturini AB, Guilardi LF, Pereira GKR, Burgo TAL, Bottino MC, Kleverlaan CJ, Valandro LF.
    Journal: Dent Mater; 2018 Sep; 34(9):e255-e263. PubMed ID: 30031547.
    Abstract:
    OBJECTIVES: To evaluate the effects of the etching with different hydrofluoric acid (HF) concentrations on the cyclic load-to-failure (CLf) of machined lithium disilicate crowns cemented to dentin analogue material. METHODS: Pairs of dentin analogue prosthetic preparations and lithium disilicate ceramic crowns with simplified and standardized designs were machined (n=18). The preparations were etched with 10% HF (60s), followed by primer application. The intaglio surface of the ceramic crowns was treated as follows: non-etched (control, CTRL); or etched for 20s with different HF concentrations - 3% (HF3), or 5% (HF5), or 10% (HF10). A silane coating was then applied onto the treated ceramic surfaces, and they were adhesively cemented to the preparations. To perform the fatigue tests (staircase approach), a hemispheric stainless-steel piston (Ø=40mm) applied cyclic loads in the center of the crowns under water (initial load: 720N; step-size: 70N; cycles: 500,000; frequency: 20Hz). Additionally, topographic, fractographic, and fractal analyses were carried out. The fatigue data were analyzed using the Dixon and Mood method. RESULTS: Although the topographic and fractal analyses depicted the action of HF etching altering the superficial complexity and topography, the preponderant topography pattern was established by machining on CAD/CAM. All groups showed similar CLf (in N) (CTRL=805.00±91.23; HF3=781.25±29.87; HF5=755.00±154.49; HF10=833.75±100.74). SIGNIFICANCE: Etching with different HF acid concentrations did not promote a deleterious effect on the cyclic load-to-failure of machined lithium disilicate crowns.
    [Abstract] [Full Text] [Related] [New Search]