  • Title: Effect of different times of nonthermal argon plasma treatment on the microtensile bond strength of self-adhesive resin cement to yttria-stabilized tetragonal zirconia polycrystal ceramic.
    Author: Elias AB, Simão RA, Prado M, Cesar PF, Botelho Dos Santos G, Moreira da Silva E.
    Journal: J Prosthet Dent; 2019 Mar; 121(3):485-491. PubMed ID: 30409721.
    Abstract:
    STATEMENT OF PROBLEM: Nonthermal argon plasma may increase the surface energy of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) dental ceramics. However, studies that evaluated the effect of increased plasma treatment times on the bond strength of resin cements to Y-TZP ceramics are lacking. PURPOSE: The purpose of this in vitro study was to evaluate the effect of different nonthermal argon plasma (NTAP) treatment times on the surface energy and bond strength of a self-adhesive resin cement to Y-TZP ceramic. MATERIAL AND METHODS: Forty-eighty Y-TZP plates were divided into 2 groups (n=24): as-sintered (AS) and airborne-particle abrasion (APA) with 50-μm Al2O3, which were subdivided into 4 groups (n=6) according to the time of NTAP treatment: 0, 20, 60, and 120 seconds. The surface energy was evaluated with a goniometer. Forty Y-TZP blocks submitted to the same surface treatments (8 groups; n=5) were cemented to composite resin blocks, using a self-adhesive resin cement. After storage in distilled water at 37°C for 24 hours, the Y-TZP-composite resin blocks were cut into beams and submitted to a microtensile bond strength (μTBS) test. Data were analyzed using 2-way ANOVA and the Tukey honestly significant differences test (α=.05). RESULTS: Treatment with NTAP increased the surface energy for AS and APA groups (P<.05). For both groups, the μTBS was as follows: 0 seconds < 20 seconds < 60 seconds = 120 seconds (P<.05). Only after 120 seconds of NTAP treatment was the μTBS of APA higher than that of AS (P<.05). CONCLUSIONS: Treatment with NTAP improved the surface energy and increased the μTBS of self-adhesive resin cement to Y-TZP ceramic, with higher times of plasma treatment resulting in higher bond strength.
    [Abstract] [Full Text] [Related] [New Search]