  • Title: Aqueous-Solution-Processed Cu2ZnSn(S,Se)4 Thin-Film Solar Cells via an Improved Successive Ion-Layer-Adsorption-Reaction Sequence.
    Author: Suryawanshi MP, Ghorpade UV, Suryawanshi UP, He M, Kim J, Gang MG, Patil PS, Moholkar AV, Yun JH, Kim JH.
    Journal: ACS Omega; 2017 Dec 31; 2(12):9211-9220. PubMed ID: 31457436.
    Abstract:
    A facile improved successive ionic-layer adsorption and reaction (SILAR) sequence is described for the fabrication of Cu2ZnSn(S,Se)4 (CZTSSe) thin-film solar cells (TFSCs) via the selenization of a precursor film. The precursor films were fabricated using a modified SILAR sequence to overcome compositional inhomogeneity due to different adsorptivities of the cations (Cu+, Sn4+, and Zn2+) in a single cationic bath. Rapid thermal annealing of the precursor films under S and Se vapor atmospheres led to the formation of carbon-free Cu2ZnSnS4 (CZTS) and CZTSSe absorber layers, respectively, with single large-grained layers. The best devices based on CZTS and CZTSSe absorber layers showed total area (∼0.30 cm2) power conversion efficiencies (PCEs) of 1.96 and 3.74%, respectively, which are notably the first-demonstrated efficiencies using a modified SILAR sequence. Detailed diode analyses of these solar cells revealed that a high shunt conductance (G sh), reverse saturation current density (J o), and ideality factor (n d) significantly affected the PCE, open-circuit voltage (V oc), and fill factor (FF), whereas the short-circuit current density (J sc) was dominated by the series resistance (R s) and G sh. However, the diode analyses combined with the compositional and interface microstructural analyses shed light on further improvements to the device efficiency. The facile layer-by-layer growth of the kesterite CZTS-based thin films in aqueous solution provides a great promise as an environmentally benign pathway to fabricate a variety of multielement-component compounds with high compositional homogeneities.