  • Title: Marginal adaptation and fracture resistance of feldspathic and polymer-infiltrated ceramic network CAD/CAM endocrowns for maxillary premolars.
    Author: Saglam G, Cengiz S, Karacaer O.
    Journal: Niger J Clin Pract; 2020 Jan; 23(1):1-6. PubMed ID: 31929199.
    Abstract:
    OBJECTIVE: The aim of this study was to evaluate the marginal adaptation and fracture resistance of feldspathic and Polymer-Infiltrated Ceramic Network (PICN) CAD/CAM endocrowns for maxillary premolars. MATERIALS AND METHODS: Twenty extracted human permanent maxillary premolars were randomly divided into two groups (n = 10); Group CEREC (GC), which was produced by feldspathic ceramic and the Group Enamic (GE), which was produced by PICN. All teeth were endodontically treated and decoronated horizontally at 2 mm above the cemento-enamel junction. Endocrown preparations were done with 4 mm depth into the pulp chamber. Endocrowns were manufactured using CAD/CAM from ceramic blocks. Following adhesive cementation, all specimens were subjected to thermocycling. Marginal adaptation evaluated under SEM at 200 × magnification. Each specimen was fixed in a universal testing machine and a compressive load was applied at 45° to long axis of the teeth until failure. Failure load was recorded and failure modes were evaluated. Statistical analyses were performed with SPSS 19.0 software and data were compared using Mann-Whitney U test. RESULTS: There were no significant differences in the marginal adaptation between two groups (P > 0.05). GE presented significantly higher fracture resistance when compared to GC (P < 0.05). Failure pattern was similar and characterized by the tooth-ceramic fracture on the force-applied side. CONCLUSIONS: CAD/CAM fabricated feldspathic ceramic and PICN endocrowns provide sufficient marginal adaptation, but the PICN endocrowns shows higher fracture resistance than the feldspathic ceramic endocrowns.
    [Abstract] [Full Text] [Related] [New Search]