  • Title: Load-bearing capacity of CAD/CAM 3D-printed zirconia, CAD/CAM milled zirconia, and heat-pressed lithium disilicate ultra-thin occlusal veneers on molars.
    Author: Ioannidis A, Bomze D, Hämmerle CHF, Hüsler J, Birrer O, Mühlemann S.
    Journal: Dent Mater; 2020 Apr; 36(4):e109-e116. PubMed ID: 31992483.
    Abstract:
    OBJECTIVES: The load-bearing capacity of ultra-thin occlusal veneers made of 3D-printed zirconia were compared to the ones obtained by fabricating these reconstructions by CAD/CAM milling zirconia or heat-pressing lithium-disilicate. METHODS: On 60 extracted human molars, the occlusal enamel was removed and extended into dentin. Occlusal veneers of 0.5 mm thickness were digitally designed. The specimens were divided into 3 groups (n = 20 each) differing in the restorative material and the fabrication technique of the occlusal veneer. (1) 3DP: 3D-printed zirconia (Lithoz); (2): CAM: milled zirconia (Ceramill Zolid FX); (3) HPR: heat-pressed lithium disilicate (IPS e.max Press). After conditioning procedures, the restorations were adhesively bonded onto the conditioned tooth. Thereafter, all specimens were aged in a chewing simulator by exposure to cyclic fatigue and temperature variations. Subsequently the specimens were statically loaded and the load which was necessary to decrease the maximum load by 20% and initiate a crack (Finitial) and the load which was needed to fracture the specimen (Fmax) were measured. Differences between the groups were compared applying the Kruskal-Wallis (KW) test and the Wilcoxon-Mann-Whitney-Test (WMW: p < 0.05). RESULTS: The median Finitial values for the groups 3DP, CAM and HPR were 1'650 N, 1'250 N and 500 N. The differences between all three groups were statistically significant (KW: p < 0.0001). The median Fmax values amounted to 2'026 N for the group 3DP, 1'500 N for the group CAM and 1'555 N for the group HPR. Significant differences were found between 3DP and CAM (WMW: p = 0.0238). SIGNIFICANCE: Regarding their load-bearing capacity, 3D-printed or milled zirconia as well as heat-pressed lithium disilicate can be recommended as restorative material for ultra-thin occlusal veneers to prosthetically compensate for occlusal tooth wear. Despite statistically significant differences between the restoration materials, all load-bearing capacities exceeded the clinically expected normal bite forces.
    [Abstract] [Full Text] [Related] [New Search]