  • Title: Close-Space Sublimation-Deposited Ultra-Thin CdSeTe/CdTe Solar Cells for Enhanced Short-Circuit Current Density and Photoluminescence.
    Author: Bothwell AM, Drayton JA, Jundt PM, Sites JR.
    Journal: J Vis Exp; 2020 Mar 06; (157):. PubMed ID: 32202534.
    Abstract:
    Developments in photovoltaic device architectures are necessary to make solar energy a cost-effective and reliable source of renewable energy amidst growing global energy demands and climate change. Thin film CdTe technology has demonstrated cost-competitiveness and increasing efficiencies due partially to rapid fabrication times, minimal material usage, and introduction of a CdSeTe alloy into a ~3 μm absorber layer. This work presents the close-space sublimation fabrication of thin, 1.5 µm CdSeTe/CdTe bilayer devices using an automated in-line vacuum deposition system. The thin bilayer structure and fabrication technique minimize deposition time, increase device efficiency, and facilitate future thin absorber-based device architecture development. Three fabrication parameters appear to be the most impactful for optimizing thin CdSeTe/CdTe absorber devices: substrate preheat temperature, CdSeTe:CdTe thickness ratio, and CdCl2 passivation. For proper sublimation of the CdSeTe, the substrate temperature prior to deposition must be ~540 °C (higher than that for CdTe) as controlled by dwell time in a preheat source. Variation in the CdSeTe:CdTe thickness ratio reveals a strong dependence of device performance on this ratio. The optimal absorber thicknesses are 0.5 μm CdSeTe/1.0 μm CdTe, and non-optimized thickness ratios reduce efficiency through back-barrier effects. Thin absorbers are sensitive to CdCl2 passivation variation; a much less aggressive CdCl2 treatment (compared to thicker absorbers) regarding both temperature and time yields optimal device performance. With optimized fabrication conditions, CdSeTe/CdTe increases device short-circuit current density and photoluminescence intensity compared to single-absorber CdTe. Additionally, an in-line close-space sublimation vacuum deposition system offers material and time reduction, scalability, and attainability of future ultra-thin absorber architectures.
    [Abstract] [Full Text] [Related] [New Search]