  • Title: Biomimetic polyvinyl alcohol/type II collagen hydrogels for cartilage tissue engineering.
    Author: Lan W, Xu M, Zhang X, Zhao L, Huang D, Wei X, Chen W.
    Journal: J Biomater Sci Polym Ed; 2020 Jun; 31(9):1179-1198. PubMed ID: 32207369.
    Abstract:
    Type II collagen (Col-II) is one of the important organic components of the cartilage extracellular matrix (ECM). Such natural material is known for its good biocompatibility, but it could not provide a good supporting environment for seed cells due to its rapid degradation and poor strength. In the present work, different contents of Col-II were incorporated into porous polyvinyl alcohol (PVA) to fabricate porous PVA/Col-II composite hydrogels for cartilage tissue engineering. The results illustrate that, after incorporation of Col-II, the elasticity modulus of the composite hydrogels firstly increases, and then decreases (under moisture state). The elasticity modulus of PVA/Col-II (at the ratio of 1:1) hydrogels reaches 11 ± 1.7 KPa, about two-fold higher than pure PVA hydrogels (4.9 ± 0.6 KPa). Meanwhile, all hydrogels exhibit relatively high water content (> 95%) and porosity (> 75%). The degradation analysis indicates that Col-II incorporation induce a high degradation ratio of the composite hydrogels. Cell culture results show PVA/Col-II hydrogels have no negative effects on cells viability and proliferation. The PVA/Col-II hydrogels may possess a potential application in the field of articular cartilage tissue engineering and regeneration.
    [Abstract] [Full Text] [Related] [New Search]