  • Title: Synthesis of IrO2 decorated core-shell PS@PPyNH2 microspheres for bio-interface application.
    Author: Hsieh TL, Hung PS, Wang CJ, Tso KC, Wang HY, Cheng CT, Lin YC, Chung RJ, Wei KH, Wu PW, Chen PC.
    Journal: Nanotechnology; 2020 Sep 11; 31(37):375605. PubMed ID: 32454465.
    Abstract:
    In this paper, an effective approach is demonstrated for the fabrication of IrO2-decorated polystyrene@functionalized polypyrrole (core@shell; PS@PPyNH2) microspheres. The synthesis begins with the preparation of monodispersive PS microspheres with a diameter of 490 nm, by a process of emulsifier-free emulsion polymerization, followed by a copolymerization process involving pyrrole and PyNH2 monomers in a PS microsphere aqueous suspension, to produce uniform PS@PPyNH2 microspheres with a diameter of 536 nm. The loading of 2 nm IrO2 nanoparticles onto the PS@PPyNH2 microspheres can be easily adjusted by tuning the pH value of the IrO2 colloidal solution and the PS@PPyNH2 suspension. At pH 4, we successfully obtain IrO2-decorated PS@PPyNH2 microspheres via electrostatic attraction and hydrogen bonding simultaneously between the negatively-charged IrO2 nanoparticles and the positively-charged PS@PPyNH2 microspheres. These IrO2-decorated PS@PPyNH2 microspheres exhibit a characteristic cyclic voltammetric profile, similar to that of an IrO2 thin film. The charge storage capacity is 5.19 mA cm-2, a value almost five times greater than that of PS@PPyNH2 microspheres. In addition, these IrO2-decorated PS@PPyNH2 microspheres exhibit excellent cell viability and biocompatibility.
    [Abstract] [Full Text] [Related] [New Search]