These tools will no longer be maintained as of December 31, 2024. Archived website can be found here. PubMed4Hh GitHub repository can be found here. Contact NLM Customer Service if you have questions.


Pubmed for Handhelds

PUBMED FOR HANDHELDS

Search MEDLINE/PubMed

  • Title: Effects of thermal and mechanical cycling on the mechanical strength and surface properties of dental CAD-CAM restorative materials.
    Author: Kim SH, Choi YS, Kang KH, Att W.
    Journal: J Prosthet Dent; 2022 Jul; 128(1):79-88. PubMed ID: 33546857.
    Abstract:
    STATEMENT OF PROBLEM: The properties of dental computer-aided design and computer-aided manufacturing (CAD-CAM) materials vary. Studies regarding the effects of aging on the properties of these materials are lacking. PURPOSE: The purpose of this in vitro study was to evaluate the changes in the mechanical and surface properties of different CAD-CAM materials after thermocycling and mechanical loading. MATERIAL AND METHODS: In total, 150 bar-shaped specimens (17.0×4.0×2.0 mm) were prepared from feldspathic glass-ceramic (VM; Vitablocs Mark II), lithium disilicate glass-ceramic (EX; IPS e.max CAD), zirconia-reinforced lithium silicate glass-ceramic (CD; Celtra Duo), polymer-infiltrated ceramic network (VE; Vita Enamic), and resin-nanoceramic (CS; Cerasmart). Each type was divided into 2 groups (n=15; each). One group was subjected to thermocycling in distilled water at 5 °C to 55 °C for 6000 cycles and 50 N mechanical loading for 1.2×106 cycles. The other group was stored in 37 °C water for 24 hours. Nanoindentation hardness, Young modulus, and 3-point flexural strength were measured for the analyses of the mechanical properties. Surface roughness, surface microstructure, and elemental composition were measured to analyze the surface characteristics. Statistical analyses were performed with 1-way ANOVA with the Tukey HSD post hoc test, independent samples t test, Kruskal-Wallis test with Bonferroni post hoc test, Mann-Whitney U test, and 2-way ANOVA (α=.05). RESULTS: Before and after aging, CS exhibited the lowest hardness (1.20 to 1.04 GPa) and Young modulus (13.76 to 13.48 GPa) values (P<.05). EX exhibited the highest flexural strengths (393.43 to 391.86 MPa), and VM exhibited the lowest (109.98 to 112.73 MPa) values (P<.05). CS exhibited the highest surface roughness (Sa and Sq; 10.60 to 28.82, 14.21 to 38.27 nm) values (P<.05). After aging, the hardness and Young modulus of VM, EX, and VE decreased significantly (P<.001). No significant difference was observed in the flexural strengths of the CAD-CAM materials (P>.05). Significant increases were observed in the surface roughness of all the materials (P<.05), with altered microstructures. Except for the flexural strength, the mechanical properties and surface characteristics of the CAD-CAM materials were significantly affected by the material type after aging. CONCLUSIONS: Before and after aging, resin-nanoceramic exhibited the lowest hardness and Young modulus, and the highest surface roughness. Lithium disilicate glass-ceramic exhibited the highest flexural strength and feldspathic glass-ceramic exhibited the lowest value. After aging, increased surface roughness and microstructure alterations were observed. Significant interactions between aging process and material type were found for the mechanical properties and surface characteristics except for the flexural strength.
    [Abstract] [Full Text] [Related] [New Search]