  • Title: Long-lasting hydrophilic surface generated on poly(dimethyl siloxane) with photoreactive zwitterionic polymers.
    Author: Nakano H, Kakinoki S, Iwasaki Y.
    Journal: Colloids Surf B Biointerfaces; 2021 Sep; 205():111900. PubMed ID: 34102530.
    Abstract:
    Poly(dimethylsiloxane) (PDMS) is known as one of the most established polymers for making elastomers. Therefore, it is commonly used for the fabrication of biomedical devices. Many PDMS surface modification processes have been proposed recently to increase PDMS reliability in medical fields. However, the modified surface's long-term stability is still limited. Hydrophobic recovery of PDMS is widely recognized as a factor that reduces the efficacy of PDMS surface modification. The photoreactive zwitterionic polymer effectively suppresses the hydrophobic recovery of PDMS, according to the current analysis. The photoreactive zwitterionic monomer, 2-[2-(Methacryloyloxy)ethyldimethylanmmonium] ethyl benzophenoxy phosphate (MBPP) was polymerized by conventional radical polymerization and coated on O2-plasma-treated PDMS specimens. The specimens were immersed in an aqueous solution of 2-methacryloyloxyethyl phosphorylcholine (MPC) and exposed under ultraviolet (UV) radiation for 3 h. Instead, of poly(MBPP) (PMBPP), benzophenone (BP) was also used as a conventional photoinitiator. The time-dependent change in the wettability and elemental composition of the specimen surface was monitored for nine weeks after photo-grafting of poly[2-methacryloyloxyethyl phosphorylcholine (MPC)] (PMPC). The advancing and receding contact angles (θA/θR) of the pristine PDMS specimen were 112°/71° and significantly decreased immediately after the grafting of PMPC regardless of types of photoinitiator. However, the hydrophobicity of the surface gradually recovered, and θA was changed from 12° to 81° for nine weeks of storage under air atmosphere when BP was used as a photoinitiator for graft polymerization of MPC. However, surface hydrophilicity (θA ≅ 20°) of the surface grafted with PMPC with PMBPP as an initiator was effectively preserved for nine weeks. This surface also showed excellent lubricity and non-fouling properties regardless of the storage periods. Therefore, zwitterionic photoreactive polymer, PMBPP, is then used as a macrophotoinitiator for the surface modification of PDMS.
    [Abstract] [Full Text] [Related] [New Search]